PA6 BKV 140 DUS008 000000德國朗盛Durethan 40%玻纖增強耐沖擊尼龍6塑料（18024445500）

PA 6, 40 % glass fibers, injection molding, improved impact strength



ISO Shortname: ISO 1874-PA 6HI, GR, 14-120, GF40　

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 400 bar % ISO 294-4 0.21　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 400 bar % ISO 294-4 0.75　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.07　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.09　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 12000　
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 185　
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.4　
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 105　
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 100　
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 15　
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10　
Izod impact strength 23 °C kJ/m² ISO 180-1U 90　
Izod impact strength -30 °C kJ/m² ISO 180-1U 90　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 11　
Flexural modulus 2 mm/min MPa ISO 178-A 11000　
Flexural strength 2 mm/min MPa ISO 178-A 290　
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.2　
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 280